1060 aluminum sheet is any other representative product in 1000 series aluminum alloys. 1060 aluminum alloy is shaped by using natural aluminum added by way of a small amount of copper detail, which has great forming processing characteristics, excessive corrosion resistance, true weld ability and conductivity. Similar to 1050 aluminum sheet, the 1060 pure aluminum sheet is widely utilized in products with low energy requirements, along with chemical contraptions, sheet metallic processing components, deep drawing or spinning concave boxes, welding parts, heat exchangers, clock surfaces and disk surfaces, nameplates, kitchenware, decorations, reflectors and so on.
The chemical composition of 1060 aluminum sheet alloy are: Iron (Fe) zero.35%, Manganese (Mn) zero.03%, Magnesium (Mg) 0.03%, Silicon (Si) zero.25%, Zinc (Zn) 0.05%, Titanium (Ti) 0.03%, Copper (Cu) zero.05%, Aluminum (Al) greater than 99.6%. The mechanical homes of aluminum sheet 1060 alloy are: the final tensile power of σb is higher than seventy five MPa, the conditional yield energy is better than 35 MPa.The warmth remedy technique of 1060 aluminum sheet is:
Fast annealing: the heating temperature is 350~410 levels centigrade; with the powerful thickness of the material, the heat maintenance time is between 30 and 120min; cooling in air or water.
High temperature annealing: the heating temperature is 350~500 DEG C; if the completed thickness is not much less than 6mm, the maintaining time is 10 ~ 30min, if the thickness is less than 6mm, heat till all the sheet is warm, cooling inside the air.
Low temperature annealing: the heating temperature is a hundred and fifty~250 degrees centigrade; the warmth maintenance time is 2 ~ 3H; cooling in air or water.